Title
SHEAR THICKENING PREGELATINIZED STARCH
WIPO Patent Application WO/2001/019404
Abstract
A new starch exhibits shear-thickening properties. It is a pregelatinized, cold water swelling starch, comprising: a highly cross linked, stabilized starch processed by heating to render it cold water swelling and leaving a majority of the starch granules intact. According to the process a highly cross linked starch is obtained. Then, the starch is heated under conditions of time, temperature and moisture effective to disrupt less than 50 % of intact starch granules comprised in said starch and to provide the characteristic that when a slurry of said starch is subjected to moderate to high shear the viscosity will increase toward a maximum.
Claims
1. A process for preparing pregelatinized, cold water swelling starch, comprising: providing a highly cross linked, stabilized starch; and heating said starch under conditions of time, temperature and moisture effective to disrupt less than 50% of intact starch granules comprised in said starch and to provide the characteristic that when a slurry of said starch is subjected to high shear the viscosity will increase toward a maximum and retain that viscosity throughout further low shear mixing and holding periods.
2. A process according to Claim 1 wherein said starch is a crosslinked by treatment with phosphorous oxychloride or sodium trimetaphosphate.
3. A process according to Claims 1 to 2 wherein said starch is a stabilized starch, such as an hydroxypropylated, acetylayted, phosphorylated, dextrinized starch or a starch substituted with octenylsuccinate groups.
4. A process according to Claims 1 to 3 wherein at least a majority of the starch granules are whole and unbroken.
5. A process according to Claims 1 to 4 wherein said starch is a potato starch.
6. A process according to Claims 1 to 4 wherein said starch is a tapioca starch.
7. A process according to 14 wherein said starch is derived from any one or combination of the following: potato starch, tapioca starch, arrowroot starch, yam starch, sweet potato starch.
8. A process according to Claims 1 to 4 wherein said starch is a noncereal starch.
9. A pregelatinized starch product of noncereal origin which exhibits notable shear thickening properties following medium to high shear mixing thereby enhancing their viscometric properties.
10. A pregelatinized starch product, which exhibits shearthickening properties, comprising: a highly crosslinked, stabilized and cold water swelling starch having a majority of its starch granules intact and being characterized in that when a slurry of said starch is subjected to high shear the viscosity will increase toward a maximum and retain that viscosity through out further low shear mixing and holding periods.
11. A pregelatinized starch product according to claim 10 which exhibits an increase in viscosity to a maximum following high shear mixing of an aqueous slurry wherein the final viscosity following mixing and holding to form a product is no less than 25% of the maximum viscosity.
12. A pregelatinized starch product according to claim 10 which is characterized in that an aqueous slurry does not significantly increase viscosity under low shear conditions, the increase being less than 50% of the maximum achievable under high shear conditions.
13. A pregelatinized starch product according to claim 10 which is characterized in an aqueous slurry exhibiting not less than 50% of the viscosity values of the preferred starch illustrated in Figure 1 following high shear mixing.
14. A pregelatinized starch product according to claim 10 which is characterized in an aqueous slurry exhibiting a viscosity after high shear at least 2 times as high as that exhibited after low shear and should not decrease in viscosity from a maximum by more than about 25%.
15. A pregelatinized starch product according to claim 10 which is characterized in an aqueous slurry exhibiting a viscosity after high shear at least 6 times as high as that exhibited after low shear and should not decrease in viscosity from a maximum by more than about 25%.
16. A foodstuff containing a pregelatinized starch as in Claim 9 wherein the foodstuff has a pH of 2.5 to 8.0.
17. A cosmetic or personal care product containing a pregelatinized starch as in Claims 10 to 15 wherein the cosmetic or personal care product has a pH of greater than 8.0.
18. A pregelatinized starch as in Claims 10 to 15 wherein said starch hydrates at a sufficiently slow rate as to be easily dispersible.
19. A pregelatinized starch as in Claims 10 to 15 wherein said starch is a potato starch or arrowroot starch with granular size greater than 25 microns.
20. A pregelatinized starch as in Claims 10 to 15 that can be used in place of other hydrocolloids such as xanthan gum for reasons of suspension, viscosity, clarity.
21. A pregelatinized starch as in Claims 10 to 15 that allows for reduction in use level over cereal starches in foodstuffs such as pourable salad dressing of 530%.
22. A pregelatinized starch for use in foodstuff, cosmetic or personal care products for use according to any one of Claims 10 to 15.
23. A foodstuff obtainable using a pregelatinized starch such as those in any one of Claims 10 to 15.
24. A cosmetic or personal care product using a pregelatinized starch such as those in any one of the Claims 10 to 15.
25. Pregelatinized starch products of noncereal origin and compositions which exhibit notable shear thickening properties following processing stress thereby enhancing their viscometric properties and utilities in foodstuff, cosmetics and personal care products AMENDED CLAIMS [received by the International Bureau on 2 March 2002 (02. 03. 01) ; original claims 125 replaced by new claims 125 (4 pages)] 1. A process for preparing pregelatinized, cold water swelling starch, comprising, providing a highly cross linked, stabilized starch ; and heating said starch under conditions of time, temperature and moisture effective to disrupt less than 50% of intact starch granules comprised in said starch and to provide the characteristic that when a slurry of said starch is subjected to high shear the viscosity will increase toward a maximum and retain that viscosity throughout further low shear mixing and holding periods.
26. 2 A process according to Claim 1 wherein said starch is a crosslinked by treatment with phosphorous oxychloride or sodium trimetaphosphate.
27. 3 A process according to Claim 1 or 2 wherein said starch is a stabilized starch, such as an hydroxypropylated, acetylayted, phosphorylated, dextrinized starch or a starch substituted with octenylsuccinate groups.
28. 4 A process according to Claim 1, 2 or 3 wherein at least a majority of the starch granules are whole and unbroken.
29. 5 A process according to Claim 1,2,3 or 4 wherein said starch is a potato starch.
30. 6 A process according to Claim 1,2,3 or 4 wherein said starch is a tapioca starch.
31. 7 A process according to Claim 1, 2, 3 or 4 wherein said starch is derived from any one or combination of the following : potato starch, tapioca starchy arrowroot starch, yam starch, sweet potato starch.
32. 8 A process according to Claim 1, 2,3 or 4 wherein said starch is a noncereal starch.
33. 9 A pregelatinized starch product of noncereal origin which exhibits notable shear thickening properties following medium to high shear mixing thereby enhancing their viscometric properties.
34. 10 A pregelatinized starch product, which exhibits shearthickening properties) comprising : a highly crosslinked, stabilized and cold water swelling starch having a majority of its starch granules intact and being characterized in that when a slurry of said starch is subjected to high shear the viscosity will increase toward a maximum and retain that viscosity through out further low shear mixing and holding periods.
35. 11 A pregelatinized starch product according to claim 10 which exhibits an increase in viscosity to a maximum following high shear mixing of an aqueous slurry wherein the final viscosity following mixing and holding to form a product is no less than 25% of the maximum viscosity.
36. 12 A pregelatinized starch product according to claim 10 which is characterized in that an aqueous slurry does not significantly increase viscosity under low shear conditions, the increase being less than 50% of the maximum achievable under high shear conditions.
37. 13 A pregelatinized starch product according to claim 10 which is characterized in an aqueous slurry exhibiting not less than 50% of the viscosity values of the preferred starch illustrated in Figure 1 following high shear mixing.
38. 14 A pregelatinized starch product according to claim 10 which is characterized in. an aqueous slurry exhibiting a viscosity after high shear at least 2 times as high as that exhibited after low shear and should not decrease in viscosity from a maximum by more than about 25%.
39. 15 A pregelatinized starch product according to claim 10 which is characterized in an aqueous slurry exhibiting a viscosity after high shear at least 6 times as high as that exhibited after low shear and should not decrease in viscosity from a maximum by more than about 25%.
40. 16 A foodstuff containing a pregelatinized starch as in Claim 9 wherein the foodstuff has a pH of 2. 5 to 8. 0 17. A cosmetic or personal care product containing a pregelatinized starch as in Claim 10,11,12,13,14 or 15 wherein the cosmetic or personal care product has a pH of greater than 8.
41. 0.
42. A pregelatinized starch as in Claim 10, 11, 12,13,14 or 15 wherein said starch hydrates at a sufficiently slow rate as to be easily dispersible.
43. A pregelatinized starch as in Claim 10,11,12,13, 14 or 15 wherein said starch is a potato starch or arrowroot starch with granular size greater than 25 microns.
44. A pregelati sized starch as in Claim 10, 11, 12,13,14 or 15 that can be used in place of other hydrocolloids such as xanthan gum for reasons of suspension, viscosity, clarity.
45. A pregelatinized starch as in Claim 10, 11, 12, 13,14 or 15 that allows for reduction in use level over cereal starches in foodstuffs such as pourable salad dressing of 530%.
46. A pregelatinized starch for use in foodstuff, cosmetic or personal care products for use according to any one of Claims 10,11, 12,13,14 or 15.
47. A foodstuff obtainable using a pregelatinized starch such as those in any one of Claims 10, 11, 12, 13,14 or 15.
48. A cosmetic or personal care product using a pregelatinized starch such as those in any one of the Claims 10, 11,12,13,14 or 15.
49. Pregelatinized starch products of noncereal origin and compositions which exhibit notable sheaf thickening properties following processing stress thereby enhancing their viscometric properties and utilities m ibodstuff, cosmetics and personal care products. STATEMENT UNDER ARTICLE 19 Claims 125 remain in the application, but substituted pages are supplied herewith to correct the problems with Rule 6. 4 (a) stated in Box 1 of the International Search Report. Applicant notes that U. S. Patent No. 4, 280,851 is of background interest only and is not of particular relevance to novelty as indicated in the Search Report. Applicant has prepared a starch product, for the first time, which is"shear thickening". This is counter intuitive. In this regard, Applicant submits pages ftom a standard text on the subject. Starches are not known to function in the manner of those produced by the invention, and none of the starches produced by U. S. Patent No. 4,280,851 has the property of"shear thickening". The patent talks only of gelatinizing to a condition known not to create a starch having new properties. Applicant has referenced this patent in the Description, and has indicated that"[tAhe invention achieves the above properties for a cold water swelling starch by obtaining a highly crosslinked, stabilized starch and heating this starch under conditions of time,.
Description
DESCRIPTION Shear Thickening Pregelatinized Starch Background of The Invention The invention relates to an improved starch product, products employing it and to processes for making and using it. In particular, it relates to shear thickening pregelatinized starch and its use in the preparation of a variety of products including foods and comestics.
It is known that starch becomes functional for thickening and texturizing and/or rheologically altering various products, including but not limited to foods, only after being gelatinized or cooked in aqueous slurry beyond a critical temperature (i. e., the gelatinization point) such that the granules swell, absorb water and increase the slurry viscosity. For convenience, starch manufacturers offer dry starches which have already been cooked for the user, so-called pregelatinized starches. This pregelatinization has commonly been carried out by jet cooking, roll drum drying, extrusion cooking and recently by atomized or spray cooking processes.
These methods produce pregelatinized starches of a type known as cold water swelling "CWS"starches, which exhibit a range of granularity (i. e., fully ruptured to totally intact granules). Cold water swelling starches are distinguished from cold water soluble starches because the former retains its granularity while the latter is fully soluble and largely non- granular. It has been accepted or shown by those skilled in the art that further processing with heat, acid and/or shear, as typical in food processing, would tend to reduce the peak viscosities of the pregelatinized starches relative to those initially observed for each prior to such processing stress (see, for example, D. J. Thomas and W. A. Atwell, Starches, 1999). This observed relative viscosity reduction versus shear has been considered to be independent of the raw material source of the starch. While chemical modifications (e. g., esterification, etherifcation, phosphorylation, hydrolysis, oxidation and/or crosslinking) made to alter starchfunctionality can mitigate viscosity reductions from shear, they do not eliminate them entirely (Whistler, et al, Starch: Chemistry and Technology, 1984). Clearly, increases in viscosity with
shear of the magnitude described by this invention previously have not been attributed to such modifications. Indeed, the art has been without a starch having this unique set of characteristics.
There is a need in the art for pregelatinized starches which are relatively stable (freeze/thaw, refrigerated storage, heat, shear), yet can be easily further processed at low, workable viscosities. There is a need for such starches that build higher, desirable product viscosities upon application of significant mechanical action (e. g., shear by various mixers, Lightnin' Mixer, Waring blender, colloid mill, etc.). In several industries including food processing, cosmetics, personal care, among others, such characteristics in a thickening or rheological ingredient would be advantageous and desirable.
This novel combination of properties for pregelatinized starches has not been reported previously and will have useful applications in numerous commercial areas (e. g., food processing, cosmetics, personal care, etc.). Food applications where this thin-to-thick ("thin- thick") rheological profile would be useful include, but are not limited to, pourable salad dressings, spoonable mayonnaise and dressings and fruit preparations. Cosmetic and personal care applications include, but are not limited to, skin and body lotions, hair creams and preparations and cosmetic creams and lotions.
Brief Description of the Drawings The invention will be better understood and its advantages more apparent from the following description, especially when read in light of the accompanying drawings, wherein: Figure 1 is a graph titled"Model Food System Viscosity Profile"which compares the effect shear has on a model food system employing a preferred starch according to the invention with two that are not.
Figure 2 is a chart showing the Brabender viscosity characterizations of a source potato starch used to produce a preferred starch of the invention in comparison to other source starches, (medium cross-linked potato starch and low cross-linked potato starch), prior to the atomized (spray) cooking process.
Figure 3 is a graph titled"Basic Salad Dressing Viscosity Profile"which shows the effect of shear on viscosity on salad dressings prepared with a preferred starch of the invention and two other starches.
Figure 4 is a graph illustrating one difference, namely lack of viscosity build-up under low shear conditions, between a preferred starch of the invention and a CWS highly- crosslinked waxy maize starch.
Summary of the Invention It is an object of the invention to provide a new pregelatinized, cold water swelling starch, a slurry of which exhibits a large increase in viscosity to a maximum following high shear mixing.
It is an object of the invention to provide a new pregelatinized, cold water swelling starch, a slurry of which exhibits a large increase in viscosity to a maximum following high shear mixing but only a modest increase following low shear mixing.
It is another object of the invention to provide a new pregelatinized, cold water swelling starch, a slurry of which exhibits an increase in viscosity to a maximum following high shear mixing wherein the final viscosity following mixing and holding to form a product is no less than 25% of the maximum viscosity.
It is another and more specific object of the invention to provide a new pregelatinized, cold water swelling starch, a slurry of which exhibits an increase in viscosity to a maximum following high shear mixing and which are relatively stable (freeze/thaw, refrigerated storage, heat, shear).
It is yet another and more specific object of the invention to provide a new pregelatinized, cold water swelling starch, a slurry of which can be easily processed at low, workable viscosities under low shear conditions without significant viscosity increased, yet exhibits an increase in viscosity to a maximum following high shear mixing.
It is yet another and more specific object of the invention to provide a new pregelatinized, cold water swelling starch, a slurry of which exhibits an increase in viscosity to a maximum following high shear mixing and thereby build higher, desirable product viscosities upon application of significant mechanical action (e. g., shear by various mixers, Lightnin' Mixer, Waring blender, colloid mill, etc.) in preparing products in several industries including food processing, cosmetics, personal care among others where such characteristics in a thickening or rheological ingredient are advantageous and desirable.
It is yet another and more specific object of the invention to provide a new pregelatinized, cold water swelling starch, a slurry of which exhibits an increase in viscosity due to high shear mixing and can beneficially improve a wide variety of products, including food, cosmetics and other consumer and industrial products that involve high shear mixing during preparation or prior to use.
These and other objects are accomplished by the invention, which provides a process for a new pregelatinized, cold water swelling starch, comprising: providing a highly cross linked, stabilized starch; and heating said starch under conditions of time, temperature and moisture effective to disrupt less than 50% of intact starch granules comprised in said starch and to provide the characteristic that when a slurry of said starch is subjected to high shear the viscosity will increase toward a maximum and retain this viscosity throughout further low shear mixing and holding periods.
In another aspect, the invention provides a pregelatinized starch product, which exhibits shear-thickening properties, comprising: a highly crosslinked, stabilized and cold water swelling starch having a majority of its starch granules intact and being characterized in that when a slurry of said starch is subjected to moderate to high shear the viscosity will increase toward a maximum and retain that viscosity throughout further low shear mixing and holding periods.
Among the preferred starches are root or tuber starches, particularly potato starch, including those derived from white potatoes, yams and sweet potatoes, among others.
The process has a number of preferred aspects, which are described below and shown in the attached drawings.
Detailed Description of The Invention This description will describe a unique new starch product and processes for preparing and using it in terms of the preferred mode, which is based on potato starch. Those skilled in the art will recognize that some, if not all, of the advantages of the invention can be achieved for starches from other sources. Similarly, the product applications described are presently preferred, but only exemplary. The invention has wide application to a variety of products, including, but not limited to, foodstuffs such as salad dressings or mixes thereof, cosmetics and personal care products. These products and others can be improved due to the presence of these new properties discovered for a category of gelatinized starch products which are the objects of this invention.
Those skilled in the art know that starch is deposited in various plants in the form of minute cold water insoluble granules. The sources of starches include seeds of plants such as wheat, sorghum and rice, tubers such as potato (including those derived from white potatoes, yams and sweet potatoes, among others), cassava and arrowroot and the pith of plants such as the sago palm and other sources including tapioca and the like. The source of the starch and its processing history will cause its properties to vary. The nature of the starch granules and the makeup of the starch can vary among the starches from the various sources. The work underlying the invention has been conducted principally on potato starch, but there is no reason known to exclude starches from any particular source. Thus, other starches including other root starches such as arrowroot starch and tapioca starch are included as source materials.
The skilled worker will vary the processing specific for potato to achieve success for other starches. The success in achieving the invention, regardless of source of starch will be determined on the basis of whether a starch meets the criteria of the invention which are: cold water solubility; with a viscosity profile that increases to a maximum with the application of moderate to high shear to a slurry of the starch and maintains that viscosity upon storage or under low shear for at least one week, preferably at least one month thereafter. All successful products will be highly crosslinked and have at least 50% of the starch granules intact in addition to being cold water swelling. However, not all starchesmeeting these last criteria will have the unique characteristic of a viscosity profile that increases to a maximum with the application of moderate to high shear to a slurry of the starch and maintains that viscosity upon storage or under low shear. Also, the preferred starches are characterized in that slurries of them do not significantly increase viscosity under low shear conditions, the increase being less than 50%, and preferably less than 25%, of the maximum achievable under high shear conditions.
As used herein, the term"cold water swelling"refers to a pregelatinized starch that maintains its granular shape when rehydrated. And, the term"cold water soluble"refers to a pregelatinized starch with little or no granular integrity. The amylose and amylopectin are solublized upon dehydration.
For the purposes of this description, the term"granularity"means the amount of starch present as intact granules as determined by microscopic examination of a known concentration of starch in aqueous dispersion. And, the term"Granular"refers to starch present as intact granules, whether pregelatinized or uncooked.
Because the amount of shear produced by various equipment will vary widely it is necessary to provide an objective meaning for the terms"low shear"and"high shear"as used herein. Thus, we define the terms low and high using several pieces of conveniently-available laboratory equipment, namely a Caframo-Heidolph, Model # RZR 1, Stirrer and a Waring Commercial Laboratory Blender, Model 34BL97 By Waring Co., New Hartford, CT.
"High shear"is defined using a Waring Blender and the following procedure.
High Shear Measurement-Brookfield viscosity method Formulation-750g a. 5% Starch 37.5g b. 5% Sugar 37.5g c. Deionized Water 337.5g d. Vinegar (3%) 337.5g Equipment Blender: Waring Commercial Laboratory Blender, Model #34BL97 Procedure a. Measure out the ingredients as listed above. b. Combine the dry starch and sugar by placing both into a bag or bottle mixing thoroughly by shaking vigorously for 1 minute. c. Combine water and vinegar in a 40-oz. blender vessel at lowest speed (setting #1). d. Add the dry mix slowly to the blending water/vinegar solution until all the mixture has dispersed. e. Increase blender speed to maximum (setting #7) and mix for 30 seconds. f. Stop blender and pour suspension into a 600ml beaker. Allow starch suspension to rest quiescently. g. Set up a Brookfield RTV viscometer with spindle #4 set at lOrpm. h. After 15 minute of quiescent resting, immerse the spindle in the starch suspension and run for 1 minute. Measure the Brookfield viscosity using spindle #4, 10rpm.
"Low shear"is defined using a Caframo-Heidolph, Model # RZR 1, Overhead Mixer and the following procedure.
Low Shear Measurement-Brookfield viscosity method Formulation-750g a. 5% Starch 37.5g b. 5% Sugar 37.5g c. Deionized Water 337.5g d. Vinegar (3%) 337.5g Equipment Stirrer: Caframo-Heidolph, Model # RZR 1 w/3-blade impeller
Procedure a. Measure out the ingredients as listed above. b. Combine the dry starch and sugar by placing both into a bag or bottle mixing thoroughly by shaking vigorously for 1 minute. c. Add the dry mix slowly to the moderately stirring (forms vortex, stirrer setting #2) water/vinegar solution until all the mixture has dispersed. Then increase stirring speed to form high vortex (stirrer setting #4) for 60 seconds. d. Stop stirring and allow starch suspension to rest quiescently. e. Set up a Brookfield RTV viscometer with spindle #4 set at lOrpm. f. After 15 minutes of quiescent resting, immerse the spindle in the starch suspension and run for 1 minute. Measure the Brookfield viscosity using spindle #4, l0rpm.
Thus, regardless of the mixing one actually uses in production or processing when employing the starches of the invention, the above tests are used to determine the degree of shear for which a viscosity change will be observed. In other words, we use this test to provide definition to the terms in this description and the claims and this test will then be used to determine if a starch product meets the terms of the claims.
Figure 1 illustrates the above significant characterizing properties of the starch of the invention. Figure 1 is a graph titled"Model Food System Viscosity Profile". The data for the figure was obtained for an aqueous food system such as what may be found in a pourable, fat- free salad dressing. The food system was manufactured using three different starch preparations as described in Example 1. Any cold water swelling starchthat exhibits a similar increase in viscosity with high shear, e. g., not less than 50% of the values of the preferred starch illustrated in Figure 1 is within the scope of this invention. The viscosity after high shear should be double or preferably 6-7 times as high as that exhibited after low shear and should not decrease in viscosity from a maximum by more than about 25%.
Figure 2 is a chart showing the Brabender viscosity characterizations of the source potato starch used to produce the preferred starch in comparison to other source starches, (medium cross-linked potato starch and low cross-linked potato starch), prior to the atomized (spray) cooking process. Preferred is a starch that has a Brabender curve similar to that of the high crosslinked starch with a peak viscosity less than 600 Bradender Units. The most preferred starch is potato but could be, especially, other non-cereal starches (e. g., tapioca or arrow root).
Figure 3 is a graph titled"Basic Salad Dressing Viscosity Profile"which describes a practical application of this invention. It can be seen that when a modified potato starch such as the preferred starch is employed in a model formulation such as in Example 1 where high shear is intrinsic to the model salad dressing production, the after high shear viscosity of the model dressing is 7-8 times as high as that observed after low shear mixing. Other salad dressing starches such as similarly modified waxy maize, and similarly modified corn starch, do not show such increases in viscosity with high shear when processed under the conditions employed for the potato starch.
Figure 4 is a graph illustrating one difference, namely lack of viscosity build-up, between a preferred starch of the invention, namely a CWS highly-crosslinked potato starch, and a CWS highly-crosslinked waxy maize starch under low shear conditions. The graph was prepared by dispersing in separate vessels, 1.4 g each of the starches with 2.8 grams of glycerine and 23.8 grams of water. The samples were then tested using the Instruction Manual procedures (March 1998) for Rapid Visco Analyser series 4 manufactured by Newport Scientific Pty. Ltd., Australia. The following Profile settings were employed: Temperature- 25°C ; Initial rpm-960 rpm for 10 seconds; Run rpm-60 rpm for 15 minutes. As noted above, the preferred starches are characterized in that slurries of them do not significantly increase viscosity under low shear conditions, the increase being less than 50%, and preferably less than 25%, of the maximum achievable under high shear conditions.
The starch products referred to in all the figures, tables and examples below are defined and characterized as per Table 1. Crosslinking was carried out for all using phosphorous oxychloride (POC13) following standard procedures. Stabilization, hydroxypropylation (HP), was carried out for all with propylene oxide following standard procedures. Table 1. Identification and characterization of starch products referred to in figures, tables and examples Starch Source Cooking Crosslinking Substitution DS Method POCl3 (ppm) Granular CWS PS AC 75-400 HP 0.8-0.16 high cross-linked potato starch* Granular CWS PS AC 45-74 HP 0. 8-0.16 medium cross- linked potato starch Non-Granular PS DD 75-400 HP 0.8-0.16 CWS high cross- linked potato starch Granular CWS PS AC 15 44 0. 8-0.16 low cross-linked potatostarch Granular CWS WM AC 75-400 HP 0. 8-0.16 high cross-linked waxy maize starch Granular CWS C AC 75-400 HP 0. 8-0.16 high cross-linked com starch Granular CWS WM AC 45-74 HP 0.8-0.16 medium cross- linked waxy maize starch
PS = Potato Starch WM = Waxy Maize C = Corn Starch AC = Atomized (Spray) Cooking DD = Roll Drum Dried DS = degree of substitution as determined by test method described in The United States Pharmacopoeia (USP 24) pp. 843-844. The same test is used for cellulose as for starch.
The assay is also known as the Zeisel Method.
"Granular CWS high cross-linked potato starch"is the preferred starch based on testing to date.
The invention achieves the above properties for a cold water swelling starch by obtaining a highly crosslinked, stabilized starch and heating this starch under conditions of time, temperature and moisture effective to disrupt less than 50% of intact starch granules comprised in said starchand to provide the characteristics described herein. A preferred
process for heating is described in a series of U. S. patents (U. S. Patent No. 4,280,851 issued July 28,1981 and U. S. Patent No. 4,600,472 issued July 15,1986 to Pitchon, et al., U. S.
Patent No. 4,847,371 issued July 11, 1989 to Schara, et al.). These patents teach a method for atomized or spray cooking of starch, the process involved, the equipment design, etc. in operating the process of Pitchon, et al., the conditions of operation will be selected to achieve the objective product criteria set out herein. The specific equipment configuration will to some extent require trial and error to arrive at the optimum conditions in terms of achieving the properties of shear-related viscosity and granularity required. In addition to these methods, other heating methods such as drum drying, jet cooking, extrusion cooking and the like can be employed when, again, operated under conditions effective to achieve the objective product criteria set out herein.
As used herein, the term"crosslinked starch"refers to modified starches in which chemical bonds (bridges) in and between starch molecules have been formed by means of bifunctional or polyfunctional chemical reagents. Crosslinked starches are made by treating starch in the granular state with these reagents which are capable of reacting with the hydroxyl groups in and between the starch molecules or molecule chains within the granule. The amount of crosslinking reagent is generally small since only one crosslink is required for every 100 to 2000 starch units to achieve the desired functional effect. The degree of crosslinking controls the rate and extent of starch granule swelling during cooking. Functionally, crosslinking is employed to impart greater heat resistance, acid stability and shear tolerance to the starch. In general, reagents such as phosphorus oxychloride, sodium trimetephosphate and adipic acid may be used as crosslinking agents. In the preferred embodiment all crosslinking was carried out using phosphorus oxychloride (POC13) as per the conditions listed in Table 1.
As used herein, the term"stabilized starch"refers to are modified starches which have been protected against retrogradtion by using monofunctional reagents which chemically react with the hydroxyl groups on the starch molecules to introduce a substituent groups. These substituent groups interfere with or sterically hinder the intermolecular association between dissolved amylose molecules in starch pastes, slurries and solutions. Functionally, stabilization is employed to reduce gelatinization temperature, improve water uptake and
retention and improve freeze/thaw stability. Examples of stabilized food starches are monostarch phosphates, acetylated starches and hydroxypropylated starches. Generally, the degree of substitution (DS) of these starches is between 0.01 and 0.2 (i. e., 1 to 20 substituent groups introduced per 100 starch units). In the preferred embodiment all stabilization was carried out using propylene oxide as per the conditions in Table 1 to effect hyroxypropylation (HP).
In a preferred embodiment, the invention provides for the production of a starch, Granular CWS high cross-linked potato starch in Table 1, by practicing the atomized cooking technology detailed in U. S. Patent Nos. 4,280,851,4,600,472 and 4,847,371 whereby 30-40% solids starchslurries at a pH = 6.0-7.5 are pumped at a pressure of 750-1500 psi and a rate of 2 gal/min through a two fluid nozzle, with steam as the heating medium at a pressure of 140-170 psig achieving cooking chamber temperatures of 300°-400°F and thereby gelatinizing or cooking the starchgranules. This product is then dried by passing the cooked slurry stream through a spray drying tower. By processing as indicated, certain modified potato starches are cooked to produce whole granular pregelatinized starches (cold water swelling starches) which behave contrary to the expected behavior of viscosity reduction with regards to processing stress such as shear. These starches substantially gain in viscosity following moderate (e. g., HobartTM mixer) to high shear (e. g., Waring blender, Silverson Rotostator Mixer, colloid mill) of the kinds usually employed in the food, cosmetics and personal care industries, to list a few. Other modified/crosslinked, pregelatinized non-cereal starches having similar properties (see Figure 1 and its description) would be suitable according to the invention. Also, other methods of producing whole granular pregelatinized starches such as, but not limited to, those detailed in U. S. Patent No. 3,617,383 and U. S. Patent No. 5,057,157 or derivative patents thereto are included in this preferred embodiment.
In the preferred embodiment, the invention provides for edible pregelatinized modified potato starches produced by atomized cooking which have been derivatized by standard methods by treatment with propylene oxide to produce a degree of substitution (DS) in the range of up to 0.22 and a preferred range of 0.8-0.16. Further it provides for pregelatinized starches which have been crosslinked by standard procedures with an amount of phosphorous oxychloride in the range of 75-lOOOppm and a preferred range of 75-400ppm
and/or substituted as per the above conditions. While the preferred starch is the Granular CWS high cross-linked potato starch in Table 1 as described above, other so crosslinked/modified non-cereal starches would also be suitable to the invention. The data in Example 1 and Table 1 detail and exemplify these findings.
In the most preferred embodiment of this invention the rheological profile for the starch thus produced, the preferred starch, can be described as a manifestation of"thin-thick" behavior. This occurs under basic pH (>7.0), at neutrality (pH=7.0) and under acid conditions.
The magnitude of the viscosity increase with high shear ("thin-thick"behavior) is not observed for the same modified potato source starch when pregelatinized by other methods which yield a starch with a minority of intact granules (e. g., roll drum dried), for other lesser crosslinked potato starches (Figure 1) or for similarly modified/crosslinked starches from cereal raw material sources (e. g., waxy maize, corn). The data in Example 1 and Tables 2-4 exemplify and support these findings in a model food system.
These are unique properties for a pregelatinized starch which have not been reported previously and which may have useful applications in numerous use areas (eg., food processing, cosmetics, personal care, etc.). The food applications where this"thin-thick" rheological profile would be useful can include, but are not limited to, pourable salad dressings, spoonable mayonnaise or dressings and fruit preparations, toothpaste. The reduction to practice of the preferred embodiment starch in a pourable salad dressing application is outlined in Example 2 and Table 5 and exemplified in Figure 3. A practical application in a practical fruit preparation is detailed in Example 3 and Table 6.
The pregelatinized starches of the invention are relatively stable in terms of freeze/thaw, refrigerated storage, heat and shear, yet can be easily further processed at low, workable viscosities. These starches build higher, desirable product viscosities upon application of significant mechanical action, e. g., shear by various mixers, Lightnin'TM Mixer, Waring blender, colloid mill, etc. Such characteristics are advantageous and desirable in a thickening or rheological ingredient for products of several industries including food processing, cosmetics, personal care, and others. Food applications where this thin-to-thick ("thin-thick") rheological profile would be useful include, but are not limited to, pourable
salad dressings, spoonable mayonnaise and dressings and fruit preparations. Cosmetic and personal care applications include, but are not limited to, skin and body lotions, hair creams and preparations and cosmetic creams and lotions.
Yet another preferred embodiment of this invention involves the use of pregelatinized starches modified and processed as noted above (the preferred starch) as a replacement for costly hydrocolloids such as xanthan gum for reasons of suspension, viscosity and clarity.
They would find utility in food applications such as salad dressings (e. g., fat free Italian salad dressing) where small particles of spices and seasonings are required to become and remain suspended over time in a relatively clear liquid product. It is highly advantageous for the liquid fraction to remain at a low, workable viscosity until shearing with equipment such as a colloid mill after which it is required to develop and maintain sufficient viscosity to suspend the spice and seasoning over substantial time. As outlined in Example 4 and supported by data in Table 7, the findings in this regard of this invention are exemplified.
Another preferred embodiment of this invention involves the use of these pregelatinized starches modified and processed as noted above (the preferred starch) as a viscofying hydrocolloid in cosmetic and personal care preparations. In such products as shown in Example 5, the starchacts to bind water, provide sufficient viscosity to suspend solids while imparting a smooth sensory feel to the preparations. The starches impart the clear advantage of allowing all necessary mixing, pumping and emulsion manipulation to occur at relatively low working viscosities prior to application of sufficient shear to induce their shear thickening properties and impart the final higher viscosity and stability to the cosmetic or personal care preparations. As per the formulation cited in Example 5 which contains an alpha hydroxy acid, another benefit of the use of the preferred starch is its shear thickening and stable viscosity under acid conditions (pH <4.0).
The following Example is are provided to further illustrate and explain a preferred form of the invention and are not to be taken as limiting in any regard. Unless otherwise indicated, all parts and percentages are by weight.
Example 1 This example describes the rheological properties of the starches, such as the preferred starch, which is the subject of the preferred embodiment of this invention. This rheology can be described as"thin-thick"behavior and is characterized more precisely in Figure 1 and 2 in terms of the viscosity of the model food system of Example 1. This thin-thick behavior occurs both at neutrality (pH=7.0) and under acid conditions. The large magnitude viscosity increase with high shear is not seen for the same source modified potato starch when cooked by methods producing non-granular pregelatinized starch (eg., roll drum dried), for potato starches crosslinked at lesser levels or for similarly modified/crosslinked starches from cereal sources (e. g., waxy maize, corn). Figures 1 and 2 and the data in Tables 2-4 exemplify and support these findings in a model food system.
As a first stage in the process, a Granular CWS high cross-linked potato starch as defined above in Table 1 is subjected to heating practicing the atomized cooking technology detailed in U. S. Patent Nos. 4,280,851,4,600,472 and 4,847,371. Specifically, a 30-40% solids starch slurry at a pH = 6.0-7.5 is pumped at a pressure of 750-1500 psi and a rate of 2 gal/min through a two fluid nozzle, with steam as the heating medium at a pressure of 140- 170 psig achieving cooking chamber temperatures of 300°-400°F and thereby gelatinizing or cooking the starch granules. This product is then dried by passing the cooked slurry stream through a spray drying tower. The product has substantially all of the starch granules intact and is cold water swelling.
For the purposes of our test, the following model food system was prepared and processed according to the following procedure.
Model Food System Ingredient % Sugar 23.50 Water 40.00 Vinegar 30.00 Salt 2.50 Starch 4. 00 Total 100.0
Procedure 1. The sugar, salt, and starch were dry blended together.
2. The dry ingredients were added to water using low shear overhead mixer.
3. The slurry was then subjected to high shear using a Waring blender or Silverson Rotostator Mixer as noted.
Table 2. Pregelatinized Starch Viscosity vs. Time and Shear (Pregelatinization by Spray Cooking, Slurry pH=3.0)
Starch 1 min. (cps) 20min. (cps) 24hr. (cps) 24hr. (cps) Low Shear* Low Shear* Low Shear* w/High Shear# Granular CWS 300 810 3900 1500medium cross-linked waxy maize starc Granular CWS high 550 1000 4000 1100 cross-linked waxy maize starch Granular CWS 2160 2180 6080 720 medium cross-linked potato starch Granular CWS high 380 450 680 2000 cross-linked potato starch
*Low Shear = Overhead mixer &num High Shear = Waring blender, 1 min. after 24hr. Low Shear All Viscosities: Brookfield viscometer, Spindle RVT4, RPM=10 Table 3. Pregelatinized Starch Viscosity vs. Granularity, Time, Shear and pH
Starch pH Low Shear* Low Shear* High Shear# Imin. (cps) 5min. (cps) Imin. (cps) Non-GranularCWS 3. 0 high cross-linked 910 4620 2300potato starch Preferred Starch 3.0 460 600 4600 Non-Granular CWS 7.0 high cross-linked 2500 5180 2900 potato starch 7.0 Granular CWS high 960 1000 5200 cross-linked potato starch *Low Shear = Overhead Mixer &num High Shear = Silverson Rotostator Mixer, 30 sec. @ 8400rpm after 5min. Low Shear All Viscosities : Brookfield viscometer, Spindle RVT4, RPM=10 Table 4. Pregelatinized Starch Viscosity vs. Degree of Crosslinking, Time and Shear (Pregelatinization by Spray Cooking, Slurry pH = 3.0,) Starch Low Shear* Low Shear* High Shear# Imin. (cps) 5min. (cps) lmin. (cps) Granular CWS low 2020 5300 320 cross-linked potato starch Granular CWS 2600 8300 2100 medium cross-linked potato starch Granular CWS high 460 600 4600 cross-linked potato starch
*Low Shear = Overhead Mixer &num High Shear = Silverson Rotostator Mixer, 30 sec. @ 8400rpm after 5min. Low Shear All Viscosities: Brookfield viscometer, Spindle RVT4, RPM=10
Example 2 This example describes a practical application of the preferred embodiment of this invention. It is highly advantageous that such starches be stable in high shear processing since traditional manufacture includes passing the product through a colloid mill, homogenizer or similar high shear equipment to produce the final dressing. It is also very advantageous for manufacturers to be able to carry out all the mixing, blending, pumping and salad dressing formulating procedures at low working viscosities prior to passing it through the colloid mill to produce the bottled product with its final higher viscosity. Starches such as the preferred starch fit the needs of this application extremely well owing to the"thin-thick"rheological behavior it displays as exemplified in Example 1 above.
Fat free French salad dressings were prepared following the formulation and procedure listed below using the preferred starch, comparably modified waxy maize, and a comparably modified cornstarch. The shearing of the salad dressings was carried out on an APV model 2F colloid mill using a 3 pass procedure through a. 005"gap. Brookfield viscosities were measured after the low-shear mixing step, after colloid mill shearing and again in 20 minutes as indicated in Table 5. It can be seen that there was a greater than 11- fold increase in viscosity observed with the preferred starch which was dramatically greater than the viscosities developed by the dressings with either of the cereal starches.
Fat Free French Salad Dressing Ingredients % Water 33.66 High Fructose Corn Syrup 39.54 Tomato Sauce (9.5% Solids) 12.00 Vinegar (120 Grain) 8.00 Starch 3.00 Salt 2.50 Onion Powder 0.85 Titanium Dioxide 0.07 Xanthan 0.15 Potassium Sorbate 0.09 Sodium Benzoate 0.09 EDTA 0. 005 Yellow Color &num 6 0. 04 Total 100.00
Procedure: 1. Add Water to blender or tank.
2. Add Sodium Benzoate and Potassium Sorbate and mix at low speed.
3. Add Vinegar and High Fructose Corn Syrup.
4. Mix together all dry ingredients.
5. Add premixed dry ingredients to blender or tank and mix briefly at low speed. The viscosity should be low at this point.
6. Process through a colloid mill. Note the dramatic viscosity increase.
7. Add tomato sauce and blend briefly at medium speed.
Table 5. Fat Free French Dressing Viscosities Starch Viscosity (cps) Viscosity (cps) Viscosity (cps) Low Shear * High Shear# High Shear+20min. Preferred starch 600 5660 6900 Granular CWS high 700 2820 3240 cross-linked waxy maize starch Granular CWS high 640 2320 2840 cross-linked corn starch
*Low Shear = Overhead Mixer # High Shear = APV 2F Colloid Mill,. 005"gap/3-pass All Viscosities: Brookfield viscometer, Spindle RVT4, RPM=10 Example 3 This example describes another reduction to practice of the preferred embodiment of this invention. In systems with minimal water available such as fruit preparations starches have been used to assist gelling by providing viscosity and to impart soft texture. The commercial processes for manufacture of these preparations are typically quite severe involving temperatures of 200° F or more, holding times of 30 minutes or greater, pH in the range of 3-4 and moderate/high shear. It is highly advantageous for producers to be able to carry out this processing at lower viscosities without sacrificing loss of final product viscosity due to partial starch breakdown. Starches such as the preferred starch are very well suited to this need owing to their rheological properties as have been demonstrated in Example 1 above.
Fruit preparations were made following the formulation and procedure listed below Using the preferred modified potato starch, and a comparably modified waxy maize starch.
Heating to 200° F was carried out for 2 minutes followed by cooling to 100°F. The preparations were then blended using low shear overhead mixing followed by high shear milling with a Silverson mixer. They had pH values of 3.4. Brookfield viscosities were taken after the low shear mixing and again after the high shear treatment as shown in Table 6. The fruit preparation with the preferred starch had a viscosity after low shear mixing of 60cps vs.
200cps for comparably modified waxy maize. Within one hour after high shear, the fruit preparation with the preferred starch had a viscosity of 2100cps which is 35 times greater than after low shear mixing and 6-7 times that of the fruit preparation with the comparably modified waxy maize starch. The preferred starch clearly demonstrated its propensity for shear thickening in this application and its overwhelming functional superiority to the comparably modified waxy maize starch in this regard.
Cranberry Fruit Preparation Ingredients % 70 Brix Syrup Cranberry Juice 66.6 Sucrose 33.4 100.0 Model System 70 Brix Syrup 48.50 Water 48.50 Starch 3. 00 Total 100.00 Procedure 1. Combine cranberry juice and sucrose in a saucepan.
2. Heat to 200° F stirring continually until sucrose is completely dissolved.
3. Allow solution to cool to 100° F.
4. Combine the correct amout of 70 brix solution with water and starch and stir using a propellar mixer at 320 rpm for 1 minute. Measure viscosity.
5. Shear slurry on a Silverson mixer at 9000 rpm for 10 minutes (square stator).
6. Measure viscosity.
Table 6. Fruit Preparation Viscosities (Preparation pH = 3.4) Starch Low Shear* High Shear# Shear + 20 Shear + I hr. min. Viscosity (cps) Viscosity (cps) Viscosity (cps) Viscosity (cps) Preferred Starch 60 560 1680 2100 Granular CWS 200 200 260 380 high cross-linked waxy maize starch
All Viscosities: Brookfield viscometer, Spindle RTV4, RPM=10 * Low Shear = Overhead Mixer, 320rpm, 1 min.
# High Shear = Siverson Rotostator Mixer, 30 sec. @ 9000rpm after Low Shear Example 4 This example describes another practical food application of the preferred embodiment of this invention. Xanthan gum, a relatively expensive hydrocolloid, is used widely in the preparation of salad dressings where particulate suspension, viscosity and clarity are required. It is especially useful in that it provides high viscosity even after shearing which is functionally desirable in salad dressings in which small particles of spice and seasonings need to be suspended over time in a clear liquid (e. g., fat free Italian dressing). At a typical 0.6% usage level, this allows for low working viscosities for processing ease while developing sufficient final product viscosity after shearing to allow for particulate suspension in the bottled dressing. The preferred starchprovides many of the key functionalities of xanthan gum in that modified potato starch provides a clear slurry and the preferred starch, a cold water swelling highly crosslinked potato starch, also imparts high viscosity after shearing. The preferred starch seems to be a well-suited, cost-effective replacement for xanthan gum is such applications.
Salad dressing was prepared following the formulation and procedure listed below.
The preferred starch was used at 2.7 % as the starch component and the dressing so prepared was compared to one similarly produced containing 0.6% xanthan gum. Both formulations were fluid with low, workable viscosities in the mixing stages. Brookfield viscosities, clarity and particulate suspension were compared one week after preparation and bottling. It can be
seen from the data in Table 7 that the dressing made with the preferred starch had a one week viscosity of 2400cps, exhibited excellent clarity and was able to keep the spice and seasoning particles suspended with no settling noted. In these respects, it was equivalent to the dressing containing the xanthan gum. As such, the preferred starch has been shown to be an effective shear thickening, hydrocolloid replacement for xanthan gum in such applications. The cost and use benefits of such a replacement would be apparent to those skilled in salad dressing formulation.
Fat Free Italian Dressing Ingredients % Water 17.75 Preferred Starch 2.70 HFCS 42 % 27.22 Vinegar 50 Grain 45.74 Salt 4.54 Onion-Minced 0.72 Garlic-Minced 0.54 Black Pepper-Coarse Grind 0.25 Monterey Seasoning Blend 0.36 Dehydrated Vegetable Blend 0. 18 Total 100.00 Procedure 1. Add water to blender or batch tank.
2. Add sodium benzoate and potassium sorbate and mix briefly at low speed.
3. Add vinegar and high fructose corn syrup (HFCS 42%).
4. Mix together all dry ingredient except spices.
5. Add premixed dry ingredients and mix briefly at low speed. Observe the viscosity.
6. Blend at highest speed for 30 seconds or process in colloid mill. Note dramatic viscosity increase.
7. Add all spices and blend or mix briefly at medium speed.
Table 7. Fat Free Italian Dressing Viscosities and Functionalities Hydrocolloid Usage (%) Viscosity (cps) Clarity Particulate 1 week* Suspension Xanthan Gum 0.6 3900 Excellent No Settling Preferred 2.7 2400 Excellent No Settling Starch * After High Shear: APV 2F Colloid Mill All Viscosities: Brookfield viscometer, Spindle RVT4, RPM=10
Example 5 This example describes a practical application of the preferred embodiment of this invention in the field of cosmetics and personal care products. Cosmetic and personal care lotions and creams for the skin, body and hair often employ starches as viscosifying agents and hydrocolloids. The starch functions as a water binder and imparts viscosity sufficient to suspend solids while adding to the smooth feel of the preparations. It has been found that the preferred starch imparts all these functional benefits to cosmetic preparations while allowing all processing mixing, pumping and emulsion manipulation to occur with ease at low working viscosities due to its thin-thick rheological properties as demonstrated in Example 1. With application of high shear just prior to completion of product manufacture the shear thickening properties are induced and the higher final product viscosities and stability desired are achieved in the cosmetic or personal care preparation. Moreover, as was demonstrated in Example 1, another benefit of the use of the preferred starch is its shear thickening and stable viscosity under acidic conditions. This makes it especially well-suited for use in acidic cosmetic lotions (eg., skin lotions with alpha hydroxyacid).
Using the formulation and following the procedure below, a skin lotion preparation containing alpha hydroxyacid was made. The preferred starchwas used at the 2% level as part of Phase A of the lotion formulation. Phase A containing the starch was subjected to low shear with an overhead mixer and heated to 120°F to uniformly blend all ingredients. Phase B was formed by melting the waxy components at 140°F. It was added to Phase A while low speed homogenizing. The liquid Phase C was added to the AB homogenate mixture and the entire formulation (ABC) was subjected tolO minutes of high speed homogenization to produce the final lotion (pH=3.4).
Viscosities were measured after forming the ABC Phase composite and again after the 10 minute high speed homogenization. It can be seen in Table 8 that the lotion viscosity following high shear homogenization increased nearly 50% over the ABC composite (4200cps vs 2800cps) which had already been subjected to a combined moderate shear. This is another clear manifestation of the shear thickening properties of the preferred starch. The advantages of using a starch with the demonstrated rheological behavior of the preferred starch, especially
in an acidic cosmetic lotion, are obvious to those skilled in the formulation of cosmetic and personal care preparations.
Skin Lotion with Alpha Hydroxy Acid Phase Ingredient % A Water 59.4 A Methyl Paraben 0.3 A Germall 2 0. 3 A Preferred Starch 2.0 B Isopropyl Palmitate 20.0 B Cetyl Alcohol 1.0 B Glyceryl Monostearate/PEG-100 Stearate 2.0 C Glycolic Acid 5.0 C Water 10. 0 100.0 Procedure 1. Disperse sequentially the Phase A dry ingredient in the water using an overhead mixer.
2. Heat all Phase B ingredients to 140°F until waxy components fully melt together.
3. Heat Phase A to 120°F.
4. Add Phase B (melted) to Phase A while homogenizing on slow speed. Air cool to 95°F.
5. Dissolve Phase C glycolic acid and add to AB.
6. Homogenize entire formulation on high for 10 minutes.
Table 8. Viscosity of Skin Lotion with Alpha Hydroxy Acid (Lotion pH =3.4) Starch Viscosity (cps) Viscosity (cps) Low/Moderate Shear* High Shear # Preferred Starch 2800 4200 * Low/Moderate Shear: Overhead Mixer ; Gifford-Wood Homogenizer, low speed # High Shear: Gifford-Wood Homogenizer, high speed/10 minutes All Viscosities: Brookfield viscometer, Spindle RTV 4, RPM=20 The above description is intended to enable the person skilled in the art to practice the invention. It is not intended to detail all of the possible modifications and variations
which will become apparent to the skilled worker upon reading the description. It is intended, however, that all such modifications and variations be included within the scope of the invention which is seen in the above description and otherwise defined by the following claims. The claims are meant to cover the indicated elements and steps in any arrangement or sequence which is effective to meet the objectives intended for the invention, unless the context specifically indicates the contrary.