Title
Tool Wear Characteristics of Oil Palm Empty Fruit Bunch Particleboard
Authors
Ratnasingam, Jegatheswaran; Chew Tek, Tee; Farrokhpayam, Saied Reza
Publication
Journal of Applied Science, vol. 8, Issue 8, p.1594-1596
Publication Date
00/2008
Abstract
A series of machining experiments on the Oil-Palm Empty Fruit Bunch (OPEFB) particleboard were carried out using a CNC router, to evaluate the tool wearing properties of the composite in comparison to the conventional wood-material particleboard. A single-fluted tungsten-carbide router bit (12 mm φ, 18 000 rpm), with a rake angle of 15° was used in this experiment, in which the depth of cut was 1.5 mm and feed speed was 4.5 m min-1. The router bit machined the edge of the board, moving along the full length before returning to repeat the cycle. The tool was examined for the extent of wear after complete failure had occurred. The result found that the wear pattern was similar in the oil-palm based particleboard and the wood-based particleboard, but the former was twice more abrasive compared to the latter. Microscopic examination of the cutter edge revealed greater incidence of micro-fracture when cutting the oil-palm based particleboard, indicating the presence of hard impurities in the composite. From an economic perspective, the tooling cost for machining oil-palm based particleboard is estimated to be twice of the cost for machining wood-based particleboard. This study shows that the machining properties of oil-palm based particleboard will be a primary concern, if the board is to find widespread application as a potential substitute for wood-based particleboard.
For further details log on website :
http://adsabs.harvard.edu/abs/2008JApSc...8.1594R
Tool Wear Characteristics of Oil Palm Empty Fruit Bunch Particleboard
Authors
Ratnasingam, Jegatheswaran; Chew Tek, Tee; Farrokhpayam, Saied Reza
Publication
Journal of Applied Science, vol. 8, Issue 8, p.1594-1596
Publication Date
00/2008
Abstract
A series of machining experiments on the Oil-Palm Empty Fruit Bunch (OPEFB) particleboard were carried out using a CNC router, to evaluate the tool wearing properties of the composite in comparison to the conventional wood-material particleboard. A single-fluted tungsten-carbide router bit (12 mm φ, 18 000 rpm), with a rake angle of 15° was used in this experiment, in which the depth of cut was 1.5 mm and feed speed was 4.5 m min-1. The router bit machined the edge of the board, moving along the full length before returning to repeat the cycle. The tool was examined for the extent of wear after complete failure had occurred. The result found that the wear pattern was similar in the oil-palm based particleboard and the wood-based particleboard, but the former was twice more abrasive compared to the latter. Microscopic examination of the cutter edge revealed greater incidence of micro-fracture when cutting the oil-palm based particleboard, indicating the presence of hard impurities in the composite. From an economic perspective, the tooling cost for machining oil-palm based particleboard is estimated to be twice of the cost for machining wood-based particleboard. This study shows that the machining properties of oil-palm based particleboard will be a primary concern, if the board is to find widespread application as a potential substitute for wood-based particleboard.
For further details log on website :
http://adsabs.harvard.edu/abs/2008JApSc...8.1594R
No comments:
Post a Comment