The manufacture of particleboards using mixture of peanut hull (Arachis hypoqaea L.) and European Black pine (Pinus nigra Arnold) wood chips

Author

• Cengiz Guler^, , 
• Yalcin Copur, 
• Cihat Tascioglu

• Department of Forest Products Engineering, Duzce University, Faculty of Forestry, 81260 Duzce, Turkey

Received 2 February 2007, Revised 11 June 2007, Accepted 11 June 2007, Available online 3 August 2007

https://doi.org/10.1016/j.biortech.2007.06.013

Abstract

This research was conducted to investigate the suitability of peanut hull to produce general purpose particleboards. A series of panels were produced using peanut hull and mixture of peanut hull and European Black pine wood chips. Particleboards were manufactured using various hull ratios in the mixture (0%, 25%, 50%, 75% and 100%). Urea formaldehyde adhesive was utilized in board production and boards were produced to target panel’s density of 0.7 g/cm³. Panels were tested for some physical (water absorption and thickness swelling), chemical (holocellulose content, lignin content, alcohol-benzene solubility, 1% NaOH solubility, hot water solubility and cold water solubility) and mechanical (modulus of rupture, modulus of elasticity and internal bond) properties. The main observation was that increase in peanut hull in the mixture resulted in a decrease in mechanical and physical properties of produced panels and panel including 25% hull in the mixture solely met the standard required by TS-EN 312 standard. Conclusively, a valuable renewable natural resource, peanut hull could be utilized in panel production while it has been mixed to the wood chips.

For further details log on website :
http://www.sciencedirect.com/science/article/pii/S0960852407004865