Carbohydr Polym. 2015;127:202-8. doi: 10.1016/j.carbpol.2015.03.043. Epub 2015 Mar 30.
Title
Cellulose nanocrystals isolated from oil palm trunk.
Author
Lamaming J1, Hashim R2, Sulaiman O1, Leh CP1, Sugimoto T3, Nordin NA1.
Abstract
In this study cellulose nanocrystals were isolated from oil palm trunk (Elaeis guineensis) using acid hydrolysis method. The morphology and size of the nanocrystals were characterized using scanning electron microscopy and transmission electron microscopy. The results showed that the nanocrystals isolated from raw oil palm trunk (OPT) fibers and hot water treated OPT fibers had an average diameter of 7.67 nm and 7.97 nm and length of 397.03 nm and 361.70 nm, respectively. Fourier Transform Infrared spectroscopy indicated that lignin and hemicellulose contents decreased. It seems that lignin was completely removed from the samples during chemical treatment. Thermogravimetric analysis demonstrated that cellulose nanocrystals after acid hydrolysis had higher thermal stability compared to the raw and hot water treated OPT fibers. The X-ray diffraction analysis increased crystallinity of the samples due to chemical treatment. The crystalline nature of the isolated nanocrystals from raw and hot water treated OPT ranged from 68 to 70%.
Carbohydr Polym. 2015;127:202-8. doi: 10.1016/j.carbpol.2015.03.043. Epub 2015 Mar 30.
Title
Cellulose nanocrystals isolated from oil palm trunk.
Author
Lamaming J1, Hashim R2, Sulaiman O1, Leh CP1, Sugimoto T3, Nordin NA1.
Abstract
Copyright © 2015 Elsevier Ltd. All rights reserved.
No comments:
Post a Comment